INDICATIONS

• Fixation of pins;
• Making of stump inlays;
• Restoration of the coronal stump;
• Used for both ceramic and composite restorations;
• Used as a restorative material for sandwich technique when coated with micro- or nano-hybrid composites.

PRODUCT BENEFITS

• Filled with special glass fibers and submicron radiopaque glass filler which both provide an average flexural strength of about 150 MPa (for both curing mechanisms) and minimum compressive strength of about 300 MPa. It creates a reliable and strong foundation for your direct and indirect restorations.
• Recommended to use with Jen-Esthe Posts, Jen-Fiber Tapes and Jen-Fiber Ropes for reliable and predictable results in different clinical cases.
  Ideal for core build-up.
• Recommended to keep in refrigerator to prolong shelf life but thermostable for using at room temperature for a long time.
• Jen-DuaCem FR chemically cures during some minutes and light cures in seconds to a hard consistency. Both curing mechanisms are recommended for all areas accessible to be light cured.
• Represented in shades CHM (Chameleon), A2, WO (White Opaquer) in  8.4 g double barrel syringes with mixers.

TECHNICAL INFORMATION

• Polymerization mode: double polymerization.
• Working time: at least 90 seconds at a temperature of 23°C.
• Curing time: about 3-5 minutes at 37°C.
• Light curing: 20 seconds for a layer not more than 2 mm thick or 40 seconds for a layer not more than 4 mm thick.
• Please note that the data given are for a temperature of 23°C and a relative humidity of 50%. These values may vary depending on the conditions and period of storage of the material, temperature, air humidity. Increasing the temperature of the material reduces its operating time.

PACKING

• Jen-DuaCem FR in twin syringes  or 8.4 (component A, component B).

Available shades:

• A2 shade;
• WO shade (White Opaquer);
•